| Proportion | 4:1 |
|---|---|
| Gluing process | Shower coating/roller coating |
| Flat tensile strength | >0.15Mpa |
| Foaming rate | 40~120% |
| Opening hours | 60min |
| Curing speed at room temperature | 4~6h |
| Proportion | 5:1 |
|---|---|
| Gluing process | Shower coating/roller coating |
| Flat tensile strength | >0.15Mpa |
| Foaming rate | 40~120% |
| Opening hours | 60min |
| Curing speed at room temperature | 4~6h |
| Proportion | 6:1 |
|---|---|
| Gluing process | Shower coating/roller coating |
| Flat tensile strength | >0.15Mpa |
| Foaming rate | 80~120% |
| Opening hours | 60min |
| Curing speed at room temperature | 4~6h |
| Proportion | 4:1 |
|---|---|
| Gluing process | Shower coating/roller coating |
| Flat tensile strength | >0.15Mpa |
| Foaming rate | 40~120% |
| Opening hours | >80min |
| Curing speed at room temperature | 4~6h |
| Proportion | 5:1 |
|---|---|
| Gluing process | Shower coating/roller coating |
| Flat tensile strength | >0.15Mpa |
| Foaming rate | 80~120% |
| Opening hours | >80min |
| Curing speed at room temperature | 6~8h |
| Proportion | 6:1 |
|---|---|
| Gluing process | Shower coating/roller coating |
| Flat tensile strength | >0.15Mpa |
| Foaming rate | 80~120% |
| Opening hours | >80min |
| Curing speed at room temperature | 6-8h |