Thermally Conductive Gel
SY-2592Y 
| Performance Characteristics | Two-component / Excellent thermal resistance / High electrical insulation and flame retardant / High elasticity / Superior vibration & impact resistance / Outstanding aging resistance |
|---|
| Thermal Conductivity (W/m·K) | 2.0 |
|---|
| Volume Resistivity (Ω·cm) | ＞1.0×10^13 |
|---|
| Flame Retardant Rating | UL 94 V-0 |
|---|
| Elongation at Break | 50% |
|---|
| Work Time | 60min |
|---|
Non-Foaming Potting Compound
SY-1379
| Performance Characteristics | Two-component / Excellent waterproof sealing / Superior vibration & impact resistance / Exceptional temperature & aging resistance |
|---|
| Hardness (Shore D) | 90 |
|---|
| Volume Resistivity (Ω·cm) | ＞1.0×10^14 |
|---|
| Electric Strength (kV/mm) | >10 |
|---|
|
| Work Time | 13min |
|---|
Low-Density & Thermally Conductive Foamable Potting Compound
SY-2371
| Performance Characteristics | Two-componen / Excellent waterproof sealing / Superior vibration & impact resistance / Exceptional temperature & aging resistance |
|---|
| Expansion Ratio | 6.5 times |
|---|
| Dielectric Strength (kV/mm) | 15 |
|---|
| Flame Retardant Rating | UL 94 V-0 |
|---|
| Rise Time | 3min |
|---|
| Hardness (Shore C) | 55 |
|---|
Thermally Conductive Potting Compound
SY-2172Y
| Performance Characteristics | Two-component / Excellent waterproof sealing / Superior vibration & impact resistance / Exceptional temperature & aging resistance |
|---|
| Tensile Strength (MPa) | 2.7 |
|---|
| Elongation at Break | 100%
|
|---|
| Electric Strength (kV/mm) | ＞18 |
|---|
| Work Time | 10min |
|---|
| Hardness (Shore A) | 64 |
|---|
SY-2394F
| Performance Characteristics | Two-component / Excellent thermal resistance / High electrical insulation and flame retardant / High elasticity / Superior vibration & impact resistance / Outstanding aging resistance |
|---|
| Elongation at Break | 13% |
|---|
| Thermal Conductivity (W/m·K) | <0.2 |
|---|
| Volume Resistivity (Ω·cm) | ＞1.0×10^13 |
|---|
| Flame Retardant Rating | UL 94 V-0 |
|---|
| Tack-Free Time | 150±30min |
|---|